Material_Name |
Primary energy for material and manufacturing, MJ/g |
Energy needed to remelt, MJ/g |
Energy recovered by combustion, MJ/g |
Resources, mPR90/g (weigthed after the EDIP method) |
Recovery percentage at recovery plant |
Percentage of material to be remelted for recycling |
Percentage of material to be incinerated with energy recovery |
Energy recovery by standard EOL scenario, MJ/g |
Resources recovery by standard EOL scenario, mPR/g |
Acrylonitrile/Butadiene
copolym... |
0,095 |
0 |
0,04 |
0,00004 |
98% |
0% |
80% |
-0,03136 |
0 |
aluminium |
0,17 |
0,03 |
0 |
0,0015 |
100% |
80% |
0% |
-0,106 |
-0,0012 |
Brass
Cu58Zn40Pb2 |
0,08 |
0,05 |
0 |
0,023 |
90% |
80% |
0% |
-0,0126 |
-0,01656 |
copper |
0,09 |
0,05 |
0 |
0,017 |
99% |
80% |
0% |
-0,02178 |
-0,013464 |
Copper EOL in
a shredder |
0,09 |
0,05 |
0 |
0,017 |
29% |
80% |
0% |
-0,00638 |
-0,003944 |
Copper EOL in
a shredder |
0,09 |
0,05 |
0 |
0,017 |
67% |
80% |
0% |
-0,01474 |
-0,009112 |
Copper in
elctronics |
0,09 |
0,05 |
0 |
0,017 |
99% |
80% |
0% |
-0,02178 |
-0,013464 |
Ferrite |
0,04 |
0,02 |
0 |
0,00013 |
98% |
80% |
0% |
-0,01176 |
-0,00010192 |
Glass |
0,01 |
0,007 |
0 |
0 |
0% |
80% |
0% |
0 |
0 |
Gold in
electronics |
66 |
0,05 |
0 |
90 |
98% |
80% |
0% |
-51,695 |
-70,56 |
iron |
0,03 |
0,02 |
0 |
0,00013 |
98% |
80% |
0% |
-0,00392 |
-0,00010192 |
lead |
0,03 |
0,02 |
0 |
0,075 |
85% |
80% |
0% |
-0,0034 |
-0,051 |
Lead, Pb in
electronics |
0,03 |
0,02 |
0 |
0,075 |
85% |
80% |
0% |
-0,0034 |
-0,051 |
nickel |
0,19 |
0,04 |
0 |
0,106 |
85% |
80% |
0% |
-0,0952 |
-0,07208 |
Nickel, Ni in
electronics |
0,19 |
0,04 |
0 |
0,106 |
85% |
80% |
0% |
-0,0952 |
-0,07208 |
Paper |
0,04 |
0 |
0,02 |
0 |
100% |
0% |
80% |
-0,016 |
0 |
Plastic, EPS
expanded polystyren |
0,079 |
0 |
0,048 |
0,00004 |
98% |
0% |
80% |
-0,037632 |
0 |
Poly(oxymethylene)
|
0,084 |
0 |
0,045 |
0,00004 |
98% |
0% |
80% |
-0,03528 |
0 |
Polyamide |
0,14 |
0 |
0,03 |
0,00004 |
98% |
0% |
80% |
-0,02352 |
0 |
Polycarbonate |
0,115 |
0 |
0,03 |
0,00004 |
98% |
0% |
80% |
-0,02352 |
0 |
polyethylene |
0,075 |
0 |
0,04 |
0,00004 |
98% |
0% |
80% |
-0,03136 |
0 |
polyethylene
terephthalate |
0,08 |
0 |
0,03 |
0,00004 |
98% |
0% |
80% |
-0,02352 |
0 |
Polymethyl
methacrylate |
0,11 |
0 |
0,04 |
0,00004 |
98% |
0% |
80% |
-0,03136 |
0 |
Polypropylene |
0,08 |
0 |
0,04 |
0,00004 |
98% |
0% |
80% |
-0,03136 |
0 |
Polystyrene |
0,09 |
0 |
0,04 |
0,00004 |
98% |
0% |
80% |
-0,03136 |
0 |
Polyurethane |
0,11 |
0 |
0,03 |
0,00003 |
98% |
0% |
80% |
-0,02352 |
0 |
PVC |
0,065 |
0 |
0,02 |
0,00002 |
98% |
0% |
80% |
-0,01568 |
0 |
silicon |
0,22 |
0 |
0 |
0 |
0% |
80% |
0% |
0 |
0 |
Silver in
electronics |
1,7 |
0,05 |
0 |
6,9 |
90% |
80% |
0% |
-1,179 |
-4,968 |
Sn60Pb40 |
0,03 |
0,02 |
0 |
0,585 |
50% |
80% |
0% |
-0,002 |
-0,234 |
Stainless
Steel 18/8 |
0,046 |
0,04 |
0 |
0,012 |
97% |
80% |
0% |
0,003104 |
-0,009312 |
Steel |
0,04 |
0,02 |
0 |
0,00013 |
98% |
80% |
0% |
-0,01176 |
-0,00010192 |
Styrene
polymer with 1,3-butadiene rubber |
0,081 |
0 |
0,046 |
0,00004 |
98% |
0% |
80% |
-0,036064 |
0 |
Styrene-acrylonitrile
copolymer |
0,09 |
0 |
0,04 |
0,00004 |
98% |
0% |
80% |
-0,03136 |
0 |
tin |
0,19 |
0,02 |
0 |
0,925 |
0% |
80% |
0% |
0 |
0 |
zinc |
0,07 |
0,04 |
0 |
0,033 |
85% |
80% |
0% |
-0,0136 |
-0,02244 |
Zinc, Zn as
surface treatment |
0,07 |
0,04 |
0 |
0,033 |
0% |
80% |
0% |
0 |
0 |
Zinc, Zn in
electronics |
0,07 |
0,04 |
0 |
0,033 |
85% |
80% |
0% |
-0,0136 |
-0,02244 |
|